Stress corrosion cracking of carbon steel in ammonia = Fissuration en corrosion sous contraintes d'un acier au carbone dans l'ammoniaque

Auteur(s) / Author(s)

LUNDE L. (1) ; NYBORG R. ;

Affiliation(s) du ou des auteurs / Author(s) Affiliation(s)

(1) Inst. energy technology, Kjeller 2007, NORVEGE

Résumé / Abstract

Stress corrosion cracking (SCC) growth of carbon steel in ammonia increases with the stress intensity factor and follows approximately the square root of the exposure time. The reduction of crack growth rate with time is mainly caused by crevice corrosion attack in the outer part of the crack. SCC of carbon steel in ammonia is prevented by cathodic polarization. With high anodic polarization, SCC occurs in ammonia with 2000 ppm water and in ammonia without oxygen. Coupling to zinc, aluminum, and magnesium anodes gives cathodic protection and prevents SCC. Aluminum and zinc metal spray both prevent cracking

Revue / Journal Title

Materials performance    ISSN  0094-1492 

Source / Source

1989, vol. 28, no12, pp. 29-32 (4 ref.)

Langue / Language

Anglais

Editeur / Publisher

National Association of Corrosion Engineers, Houston, TX, ETATS-UNIS  (1974) (Revue)

Mots-clés anglais / English Keywords

Stress corrosion cracking

;

Carbon steel

;

Ammonia

;

Sacrificial anode

;

Experimental study

;

Stress intensity factor

;

Crack propagation

;

Crevice corrosion

;

Anodic polarization

;

Cathodic protection

;

Velocity

;

Crack depth

;

Mots-clés français / French Keywords

Fissuration corrosion sous tension

;

Acier non allié

;

Ammoniac

;

Anode sacrificielle

;

Etude expérimentale

;

Facteur intensité contrainte

;

Propagation fissure

;

Corrosion caverneuse

;

Polarisation anodique

;

Protection cathodique

;

Vitesse

;

Profondeur fissure

;

AcierNA

;

Mots-clés espagnols / Spanish Keywords

Fisuración por tensocorrosión

;

Acero no aliado

;

Amoníaco

;

Anodo sacrificial

;

Estudio experimental

;

Factor intensidad tensión

;

Propagación fisura

;

Corrosión cavernosa

;

Polarización anódica

;

Protección catódica

;

Velocidad

;

Profundidad fisura

;

Localisation / Location

INIST-CNRS, Cote INIST : 10129

Nº notice refdoc (ud4) : 6691733



Faire une nouvelle recherche
Make a new search
Lancer la recherche
Bas