Auteur(s) / Author(s)

RANI R. ; HEGDE H. ; NAVARATHNA A. ; CADIEU F. J. ;

Affiliation(s) du ou des auteurs / Author(s) Affiliation(s)

Queens coll. CUNY, physics dep., Flushing NY 11367, ETATS-UNIS

Résumé / Abstract

High coercivity film samples of the ordered Sm2Fe17Nx phase with intrinsic coercivities, iHc' up to 23 kOe at 293 K, and 35 kOe at 10 K, were synthesized by rf sputtering. Random orientation Sm2Fe17 films were formed by the subsequent crystallization of originally amorphous deposits. The iHc of the original Sm2Fe17 films was 0.75 kOe at 293 K. X-ray diffractometer traces from 2θ=28o to 73o, Cuna, exhibited 14 lines. Before nitriding all 14 lines were fit to the 2-17 rhombohedral structure with a=8.555 Å, c=12.445 Å, with a weighted root-mean-square deviation in 2θ of 0.01o

Revue / Journal Title

Journal of applied physics    ISSN  0021-8979   CODEN JAPIAU 

Source / Source

Congrès
Annual conference on magnetism and magnetic materials No37, Houston TX , ETATS-UNIS (01/12/1992)
1993, vol. 73 (2A), no 10 (10 ref.), pp. 6023-6025

Langue / Language

Anglais

Editeur / Publisher

American Institute of Physics, Melville, NY, ETATS-UNIS  (1937) (Revue)

Mots-clés anglais / English Keywords

Magnetization

;

Coercive force

;

Demagnetization

;

Thick film

;

Preparation

;

Chemical composition

;

X ray diffraction

;

Magnetic hysteresis

;

Nitriding

;

Experimental study

;

Ternary alloy

;

Iron Nitrogen Neodymium Alloys

;

Transition metal Alloys

;

Mots-clés français / French Keywords

Aimantation

;

Champ coercitif

;

Désaimantation

;

Couche épaisse

;

Préparation

;

Composition chimique

;

Diffraction RX

;

Hystérésis magnétique

;

Nitruration

;

Etude expérimentale

;

Alliage ternaire

;

Fer Azote Néodyme Alliage

;

Métal transition Alliage

;

Mots-clés espagnols / Spanish Keywords

Imanación

;

Campo coercitivo

;

Desimantación

;

Capa espesa

;

Preparación

;

Composición química

;

Difracción RX

;

Histérisis magnética

;

Nitruración

;

Estudio experimental

;

Aleación ternaria

;

Hierro Nitrógeno Neodimio Aleación

;

Metal transición Aleación

;

Localisation / Location

INIST-CNRS, Cote INIST : 126, 35400003396430.2080

Nº notice refdoc (ud4) : 4841321



Faire une nouvelle recherche
Make a new search
Lancer la recherche
Bas