Dense manganese zinc ferrites and lead lanthanum zirconate titanate ceramics with fine grains

Auteur(s) / Author(s)

TOYOTA S. (1) ; MIYOSHI Y. ; TAKATA M. ;

Affiliation(s) du ou des auteurs / Author(s) Affiliation(s)

(1) Sumitomo Special Metals Co. & Ltd, Osaka 618, JAPON

Résumé / Abstract

Dense manganese zinc ferrites (MnZn ferrites) and lead lanthanum zirconate titanate (PLZT) with fine grains were fabricated by post-hot isostatic pressing (HIP) technique using finely ground starting powders prepared by a media agitation milling method. The average particle size of MnZn ferrites milled by media agitation milling was 0.03 μm, and the average grain size of the HIP'ed body was 1.2 μm. The ferrites showed low power-loss at high frequencies and initial permeability of 500 at 10 MHz. HIPing treatment of PLZT ceramics improved the transmittance without significant increase in grain size. The optical transmittance and grain size of HIP'ed PLZT were 69% at the wavelength of 750 nm and 2 μm, respectively. PLZT with fine grains showed microscopically uniform birefringence (...)

Revue / Journal Title

Zairyo    ISSN  0514-5163   CODEN ZARYAQ 

Source / Source

1994, vol. 43, no492, pp. 1047-1052 (8 ref.)

Langue / Language

Japonais

Editeur / Publisher

Society of Materials Science, Kyoto, JAPON  (1963) (Revue)

Mots-clés anglais / English Keywords

Oxide ceramics

;

Optical ceramics

;

Ferrite materials

;

Manganese Oxides

;

Zinc Oxides

;

Iron Oxides

;

Quaternary compounds

;

Lead Titanates

;

Lead Zirconates

;

Lanthanum Titanates

;

Lanthanum Zirconates

;

Manufacturing

;

Sintering

;

Hot isostatic pressing

;

Optical properties

;

Light transmission

;

Experimental study

;

Mots-clés français / French Keywords

Céramique oxyde

;

Céramique optique

;

Ferrite céramique

;

Manganèse Oxyde

;

Zinc Oxyde

;

Fer Oxyde

;

Composé quaternaire

;

Plomb Titanate

;

Plomb Zirconate

;

Lanthane Titanate

;

Lanthane Zirconate

;

Composé n éléments

;

PLZT

;

La O Pb Ti Zr

;

Fe Mn O Zn

;

Fabrication

;

Frittage

;

Pressage isostatique chaud

;

Propriété optique

;

Transmission lumière

;

Etude expérimentale

;

Mots-clés espagnols / Spanish Keywords

Cerámica óxido

;

Cerámica óptica

;

Ferrita cerámica

;

Manganeso Óxido

;

Zinc Óxido

;

Hierro Óxido

;

Plomo Titanato

;

Plomo Zirconato

;

Lantano Titanato

;

Lantano Zirconato

;

Fabricación

;

Sinterización

;

Prensado isostático caliente

;

Propiedad óptica

;

Transmisión luz

;

Estudio experimental

;

Localisation / Location

INIST-CNRS, Cote INIST : 12572, 35400004192747.0020

Nº notice refdoc (ud4) : 3327111



Faire une nouvelle recherche
Make a new search
Lancer la recherche
Bas